Polyethylene Film Grade LL 0220KJ (High Slip Antiblock), Thickness: 38 microns, Blow up Ratio (150*2.3 mm die): 2:1, Max Output Rate: 50 kg/hr, Melt Flow rate (2.16 kg): 2 g/10 min, Test Method: ISO 1133, Density: 920 kg/m3, Test Method: ISO 1872/1, Vicat Softening Temp.: 93 C, Test Method: ISO R 306-74, Tensile Strength at yield MD/TD: 10/11 MPa, Test Method: ISO R 1184, Tensile Strength at break MD/TD: 30/25 MPa, Test Method: ISO R 1184, Elongation at break MD/TD: 650/800 %, Test Method: ISO R 1184, Tear Strength MD/TD: 100/270 g/25 mic, Test Method: ASTMD 1922-67, Dart Impact Stength: 100 g, Test Method: ASTMD 1709-75