Polyethylene Injection and Roto Moulding Grade HD3840UA (UV Stabilization), Melt Flow rate (2.16 kg): 4 g/10 min, Test Method: ISO 1133, Density: 938 kg/m3, Test Method: ISO 1872/1, Tensile Strength at yield: 18 MPa, Test Method: BP 13B/1, Elongation at break: 1400 %, Test Method: BP 13B/1, Flexural Modulus: 750 MPa, Test Method: ISO 178, ESCR (Environmental Stress Cracking Resistance), F50, 23 C: 200 hours, Test Method: ASTMD 1693, Charpy impact resistance: 20 KJ/M2, Test Method: ASTMD 256.